    A big thank you for all the wonderful info on filling the pitch
    bowl...I will put the info to good use. 

    Also, thank you on the pitted solder question. I've reflowed it with
    handiflux and they are better (not perfect but better). Hopefully
    next time I can avoid that. I think I definetly had too much solder
    as I was trying to build a fillet around the bezel (I think that is
    the word?). I also may have had too much My T Flux on it...if that
    is possible. 

Best,
donna

____________________________________________________________________
T h e   O r c h i d   L i s t
Open Electronic Forum for Jewelry Manufacturing Methods and Procedures
____________________________________________________________________
Orchid FAQ:
~ http://www.ganoksin.com/orchid/faq.htm
Orchid Archives:
~ http://www.ganoksin.com/orchid/archive
Orchid Galleries:
~ http://www.ganoksin.com/orchid/gallery.htm
Invite a Friend:
~ http://www.ganoksin.com/invite.htm
____________________________________________________________________
Tips From The Jeweler's Bench - Article Archive
~ http://www.ganoksin.com/borisat/tip_sear.htm
The Jeweler's Selected Bibliography List
~ http://www.ganoksin.com/jewelry-books
Buy Orchid Jewelry:
~ http://www.ganoksin.com/shop
____________________________________________________________________
-Unsubscribe:
-Email: orchid-request AT ganoksin.com Body=unsubscribe subject=blank
____________________________________________________________________