Re: [Orchid] Casting temperature for non-tarnishing silver
-> Navigate by Topic: [Thread Prev] [Thread Next]
-> Navigate by Date: [Message Prev] [Message Next]
-> Locate this message on the Date Tree or Thread Tree

Michael Mathews Tuesday, September 01, 1998
    
========[ Invite a Friend - http://www.ganoksin.com/invite.htm  ]========


>         I will be casting the non-tarnishing silver in a weeks
>     time. My question for this metal is what casting temperature is
>     being used for this metal. 

    Hello Surbhi:    If you mean that new "Antifirescale" silver, my
    info. says cast at normal flask temp for silver 880-850 degrees
    F. Flow point of this metal is 1650 degrees F This information was
    taken from my Rio Grande catalog. 

Michael Mathews    Victoria,Texas   USA
http://www.geocities.com/Colosseum/Loge/9493/orchidlist.html
Search Jewelry related web sites including many from Orchid members here.
Click to Visit

--Back to Top--

Bookmark and Share Printer View Printer View
Navigate:
Orchid Resources:

 
Donate! If you believe in what we're doing, you can help!
© Copyright 1996 - 2013, The Ganoksin Project
Home